R&G - Release spray - 400ml

SKU: 331896

Category: epoxy & resins

HAN: 1651051
GTIN: 4044199006159
HAN: 1651051

19,90 €

49,75 € per 1 l

incl. 19% VAT , plus

Available immediately
nur 1 Stück lagernd!

Lieferzeit: 1-2 Werktage

piece

Available immediately
nur 1 Stück lagernd!

Lieferzeit: 1-2 Werktage

External release agent for epoxy and polyester resins, PMMA, polyurethanes.

Easy to polish, soft release wax for spraying (curing temperatures up to max. 120 °C) Silicone-free Field of application
Suitable substrates: practically all smooth surfaces such as plastic (GRP), metal and glass, but also porous and absorbent materials such as wood, plaster and molded ceramics, if applied several times in full. However, absorbent surfaces are difficult to mold if the resin can flow into the pores and anchor mechanically.

Release Spray TRS is also excellent for making silicone rubber surfaces wettable. In addition, the release spray acts as an insulating layer and extends the durability of molds, especially when working with epoxy resins.

The fine spray mist facilitates application in complicated, angled molds. The release spray can also be used as a sliding layer by repeated spraying without intermediate polishing. This is necessary, for example, when producing wound components such as cylindrical tubes, in order to be able to pull out the winding cores again.

Processing:
Shake can well before application. Spray on from a distance of 20 - 30 cm. In hard-to-reach places, spraying can also be carried out at an angle or overhead for short periods.

New molds are treated 2 - 3 times, polishing each coat by hand with a soft cotton cloth immediately after application. After complete drying, the film can no longer be polished without streaks.

Allow to flash off on silicone rubber for approx. 30 minutes, then the surface can be coated with e.g. EP gelcoat without forming eyes.

Residues in the mold can be removed with white spirit or mechanically with steel wool.

Physico-chemical characteristics:

Form: Aerosol
Color: White
Odor: Characteristic
Density at 20 °C (DIN standard 51757): 0.64 g/ml
Active substance content: 2.95
Flash point: > -97 °C
Viscosity at 20 °C (spout cup 4 mm DIN EN ISO 2431): < 59 sec
Storage temperature: between 10 °C and 30 °C