This dilute, solvent and filler-free epoxy resin has been revised to achieve an improved and innovative Härter quality. It is free of nonylphenol and benzyl alcohol, and the adhesive and hardening properties have been optimized. As it hurts from 5°C onwards, it is also known as low temperature hunter.
In addition to rapid trimming of glass, armid and carbon fibres, bonding is also no problem. It is excellently suited for wood, metal, polystyrene and other materials, as the surface tension is very low, adhesion is good and the loss of adhesion is very low.
All common processing methods such as hand laminating, pressure and vacuum impregnation as well as pressing and winding are possible without any problems.
It has äsimilar strengths with Härtern S (15 minutes), L (40 minutes), EPH 500 (60 minutes), EPH 161 (90 minutes) and W 300 (300 minutes) as the laminating systems commonly used in aviation. The heat deflection temperature ranges from 60 °C (S, L, EPH 500) to about 120 °C (EPH 161, after heat treatment).
This epoxy resin is not without reason the best-selling laminating and adhesive resin from the R&G product range!
Epoxy resin L + Härter S
- Processing time: 15 minutes
- Mixing ratio:
- 100 : 40 parts by weight resin : Härter
- ausause time: 24 hours
- Cold“rtend
General description of the system Epoxy resin L with the Härtern S, L, EPH 500, EPH 161 and W 300:
- Dünnfl;ssig, free of solvents and fillers
- Fast Trending of Glass, Aramid and Carbon Fibers
- High static and dynamic strength
- The epoxy resin L with the associated laminating agents S, L, EPH 500 and EPH 161 is the most widely used laminating and adhesive resin from the R&G product range.